Reasonable price Donfoam 602 Hcfc-141b Base Blend Polyols - Donpanel 413 CP/IP base blend polyols for PUR – INOV

Donpanel 413 CP/IP base blend polyols for PUR

INTRODUCTION

DonPanel 413  is a kind of blend polyether polyols with cyclopentane as foaming agent, taking polyol as the main raw material and mixed with special auxiliary agent. It is suitable for thermal insulation of building boards, cold storage boards and other products.The polyurethane product prepared by reacting it with isocyanate has the following advantages:

-- No greenhouse effect and does not damage the ozone layer

-  Good fluidity and uniform foam density

-- Excellent insulation, dimensional stability and adhesion

PHYSICAL PROPERTY

 

DonPanel 413

Appearance                 Hydroxyl value                 mgKOH/g

Dynamic viscosity (25℃)   mPa.S

Density (20℃)             g/ml

Storage temperature             ℃

Storage stability               months

Light yellow transparent viscous liquid

300-400

300-400

1.04-1.12

10-25

6

RECOMMENDED RATIO

 

PBW

DonPanel 413

100

Isocyanate

110-130

TECHNOLOGY AND REACTIVITY (the exact value varies depending on processing conditions)

 

Manual mix

High pressure

Raw material temperature    ℃

CT      S

GT      S

TFT      S

Free density   Kg/m3

20-25

10-50

80-200

120-280

23-28

20-25

10-40

60-160

100-240

23-28

FOAM PERFORMANCES

Mold density

Close-cell rate

Thermal conductivity (10℃)

Compression strength)

Dimensional stability        24h -20℃ 

                      24h 100℃

Flammability

GB/T 6343

 GB/T 10799

GB/T 3399

GB/T 8813

GB/T 8811

 

GB/T 8624

 ≥42 Kg/m3

≥90%

≤22mW/m.k

≥150 KPa

≤0.5%

≤1.0%

B3