INTRODUCTION
DonSpray504 is spray blend polyols, blowing agent is 245fa instead of HCFC-141B, it reacts with isocyanate to produce foam which has excellent performances, which are as follows,
1) fine and uniformity cells
2) low thermal conductivity
3) perfect flame resistance
4) good low-temperature dimensional stability.
It applies to all kinds of thermal insulation engineering which uses the spray technology, such as cold rooms, pots, large-scale pipelines and construction metope etc.
PHYSICAL PROPERTY
Appearance |
Pale yellow to brown viscous liquid |
Hydroxyl Value mgKOH/g |
200-300 |
Dynamic viscosity(25℃) mPa.S |
100-200 |
Specific gravity (20 ℃ ) g/ml |
1.12-1.20 |
Storage temperature ℃ |
10-25 |
Storage stability month |
6 |
RECOMMENDED RATIO
Raw materials |
pbw |
DonSpray 504 blend polyols |
100 g |
Isocyanate MDI |
100-105g |
Reactivity Characteristics (The temperature of the system is 20℃,and the exact value varied depending on processing condition)
Cream Time s |
3-5 |
Gel Time s |
6-10 |
FOAM PERFORMANCES
Items |
Metric Unit |
Imperial Unit |
||
Spray Density | GB 6343 | ≥35kg/m3 | ASTM D 1622 | ≥2.18 lb/ft3 |
Closed-cell Rate | GB 10799 | ≥90% | ASTM D 1940 | ≥90% |
Initial Thermal Conductivity(15℃) | GB 3399 | ≤24mW/(m.K) | ASTM C 518 | ≥2.16/inch |
Compressive Strength | GB/T8813 | ≥150kPa | ASTM D 1621 | ≥21.76PSI |
Adhesive Strength | GB/T16777 | ≥120kPa | ASTM D 1623 | ≥17.40PSI |
Dimentional Stability 24h -20℃ | GB/T8811 | ≤1% | ASTM D 2126 | ≤1% |
24h 70℃ | ≤1.5% | ≤1.5% | ||
Water Absorption | GB 8810 | ≤3% | ASTM E 96 | ≤3% |
Fire Resistance | GB 8624 | Class B2 | ASTM D2863-13 | Class B2 |
PACKAGE
220kg/drum or 1000kg/IBC, 20,000kg/flexi tank or ISO Tank.