100% Original Castable Polyurethane Shoe Upper Prepolymer - Donfoam 812 HCFC-141B base blend polyols for block foam – INOV

Donfoam 812 HCFC-141B base blend polyols for block foam

INTRODUCTION

Donfoam 812 blend polyether polyols used for produce PUR block foam. The foam has uniform cell , low thermal conductivity, thermal insulation performance is good, flame retardant performance is good, low temperature no shrinking crack etc.

Widely used in the process of all kinds of insulation work such as: building external wall, cold storage, tanks, large pipes etc.

PHYSICAL PROPERTY

Appearance

Dynamic viscosity (25℃)      mPa.S

Density (20℃)              g/ml

Storage temperature              ℃

Storage stability                 month

Light yellow to brown transparent liquid

250±50

1.17±0.1

10-25

6

RECOMMENDED RATIO

Items

PBW

Blend Polyether Polyol

Isocyanate

100

130

TECHNOLOGY AND REACTIVITY (the exact value varies depending on processing conditions)

 

Manual Mixing

Raw Material Temperature   ℃

Mould Temperature        ℃

CT                       s

GT                       s

TFT                      s

Free Density            kg/m3

20-25

Ambient Temperature(15-45℃ )

35-60

140-180

240-260

26-28

FOAM PERFORMANCES

Item

Test Standard

Specification

Overall Molding Density

Molding Core Density

GB 6343

40-45kg/m3

38-42kg/m

Closed-cell Rate

GB 10799

≥90%

Initial Thermal Conductivity(15℃)

GB 3399

≤24mW/(m.K)

Compressive Strength

GB/T8813

≥150kPa

Dimensional Stability  

                    24h      -20℃

                    RH90     70℃   

GB/T8811

≤1%

≤1.5%

Water Absorption Rate

GB 8810

≤3%

Flammability

ASTM E84

Class A