INTRODUCTION
This product is a type of blend polyols with water as foaming agent, which is specially researched for rigid PUF to produce thermal insulation pipes. It is widely used in steam pipes, liquefied nature gas running pipes, oil pipes and other fields. The characteristics are as follows:
(1) good flowability, by regulating formula to suit different pipe diameters.
(2) high temperature-resistance performance, long standing in 150℃
(3) excellent low temperature dimensional stability
PHYSICAL PROPERTY
Appearance |
Light yellow to brown transparent liquid |
Hydroxyl value mgKOH/g |
250-450 |
Dynamic viscosity(25℃) mPa.S |
300-600 |
Density (20℃) g/ml |
1.10-1.16 |
Storage temperature ℃ |
10-25 |
Storage stability month |
6 |
TECHNOLOGY AND REACTIVITY (Component temperature is 20℃, the actual value is varied according to pipe diameter and processing condition.)
|
Manual mixing |
High pressure machine |
Ratio(POL/ISO) |
1:1.40-1.1.60 |
1:1.40-1.60 |
Rise time s |
20-40 |
15-35 |
Gel time s |
80-200 |
80-160 |
Tack free time s |
≥150 |
≥150 |
Free density kg/m3 |
34.0-36.0 |
33.0-35.0 |
FOAM PERFORMANCES
Mold density | GB 6343 | 60-80kg/m3 |
Closed-cell rate | GB 10799 |
≥90% |
Thermal conductivity (15℃) | GB 3399 |
≤33mW/(m.K) |
Compression strength | GB/T8813 | ≥250kPa |
Water absorption | GB 8810 |
≤3(V/V)% |
Dimensional stability 24h -30℃ | GB/T8811 |
≤1.0% |
24h 100℃ |
≤1.5% |
The data provided above are typical value, which are tested by our company. For our company's products, the data included in the law do not have any constraints.