INTRODUCTION
Donfoam823 blend polyether polyol use CP or CP/IP as blowing agent, used in the production of high flame retardant PIR block foam, with performances of uniform foam cell, low thermal conductivity, good thermal insulation and high flame retardant, low temperature no shrinking crack etc. Widely used in the process of all kinds of insulation work such as: building external wall, cold storage, tanks, large pipes etc.
PHYSICAL PROPERTY
| Appearance
Dynamic viscosity （25℃） mPa.S Density （20℃） g/ml Storage temperature ℃ Storage stability month |
Light yellow to brown transparent liquid
500±100 1.20±0.1 10-25 6 |
RECOMMENDED RATIO
| Items |
PBW |
| DK-1103 Blend Polyether Polyol
CP or CP/IP Isocyanate |
100 11-13 165-175 |
TECHNOLOGY AND REACTIVITY (the exact value varies depending on processing conditions)
|
Manual Mixing |
|
| Raw Material Temperature ℃
Mold Temperature ℃ CT s GT s TFT s Free Density kg/m3 |
20-25 Ambient Temperature (15-45℃ ) 35-60 140-200 240-360 28-35 |
FOAM PERFORMANCES
|
Item |
Test Standard |
Specification |
| Overall Molding Density
Molding Core Density |
ASTM D1622 |
≥50kg/m3 ≥40kg/m |
| Closed-cell Rate | ASTM D2856 |
≥90% |
| Initial Thermal Conductivity（15℃） | ASTM C518 |
≤24mW/(m.K) |
| Compressive Strength | ASTM D1621 |
≥150kPa |
| Dimensional Stability
24h -20℃ RH90 70℃ |
ASTM D2126 |
≤1% ≤1.5% |
| Water Absorption Rate | ASTM D2842 |
≤3% |
| Flammability | ASTM D1692 |
Self extinguishing |