DESCRIPTION
Component: DY2513 is consist by Components ABC. Component A is polyol, B is polyurethane prepolymer which ended up with isocynate, C is chain extender.
Characteristic: The final product enjoys good anti resistance ability, good rebound. And the hardness can be adjusted by the different ratio. The color can be adjusted by pigment.
Application: This material was used to produce Polyurethane sieves, PU rollers, cleaning pigs (discs) and other elastomer.
SPECIFICATION
|
Type |
DY2513-B |
DY2513-A |
DY2513-C |
|||||
|
NCO/% |
13.1 |
|
|
|||||
|
Operation temperature /℃ |
45 |
50 |
45 |
|||||
|
Viscosity mPa·s/ |
800 |
1200 |
30 |
|||||
|
Prepolymer |
DY2513-B |
|||||||
|
Chain extender |
DY2513-A﹢DY2513-C |
|||||||
|
Hardness /shore A |
60 |
65 |
70 |
75 |
80 |
85 |
90 |
95 |
|
DY2513-B（ratio, by weight ） |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
|
DY2513-A（ratio, by weight ） |
180 |
150 |
120 |
100 |
80 |
60 |
40 |
20 |
|
DY2513-C（ratio, by wight） |
5.7 |
7 |
8.4 |
9.3 |
10.2 |
11.1 |
12 |
12.9 |
|
Catalyst/total amount A+B+C % |
0.6 |
0.6 |
0.6 |
0.45 |
0.3 |
0.3 |
0.24 |
0.24 |
|
Mold temperature/℃ |
100 |
|||||||
|
Gel time/min |
2，30 |
2，30 |
2，20 |
2，20 |
2，30 |
2，30 |
2，10 |
2，10 |
|
Open Mold Time/ min |
60 |
50 |
40 |
40 |
40 |
40 |
40 |
40 |
DESCRIPTION
It is used to produce Polyurethane sieves, PU rollers and other elastomer. It should be processed by mid-temperature casting machine.
The final product enjoys good anti resistance ability, good rebound. And the hardness can be adjusted by the different ratio. The color can be adjusted by pigment.
Application: automotive kits, pipe cleaners, etc., polyurethane large or small product components.
SPECIFICATION
|
Type |
DY3516-B |
DY3516-A |
DY3516-C |
|||||||
|
NCO/% |
16.5±0.2 |
|
|
|||||||
| Operation temperature /℃ |
45 |
70 |
45 |
|||||||
|
Viscosity mPa·s/ |
700 |
730 |
30 |
|||||||
|
Prepolymer |
DY3516-B |
|||||||||
|
Chain extender |
DY3516-A+DY3516-C |
|||||||||
|
Hardness /shore A |
55 |
60 |
65 |
70 |
75 |
80 |
85 |
90 |
||
|
DY3516-B(ratio, by weight） |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
||
|
DY3516-A(ratio, by weight） |
380 |
180 |
160 |
130 |
110 |
100 |
80 |
60 |
||
| DY3516-C(ratio, by weight) |
0 |
9.1 |
10 |
11.4 |
12.3 |
12.7 |
13.6 |
14.5 |
||
|
Catalyst/total amount A+B+C % |
0.4 |
0.4 |
0.4 |
0.4 |
0.3 |
0.3 |
0.3 |
0.3 |
||
|
Mold temperature/℃ |
100 |
|||||||||
|
Gel time/min |
5 |
5 |
5 |
5 |
5 |
4 |
4 |
4 |
||
|
Open Mold Time/ min |
50 |
35 |
35 |
30 |
30 |
30 |
30 |
30 |
||
|
Post cure time(90℃)/h |
16 |
|||||||||
AUTOMATIC CONTROL